This mock test of Test: Strength of Materials Level - 3 for Mechanical Engineering helps you for every Mechanical Engineering entrance exam.
This contains 25 Multiple Choice Questions for Mechanical Engineering Test: Strength of Materials Level - 3 (mcq) to study with solutions a complete question bank.
The solved questions answers in this Test: Strength of Materials Level - 3 quiz give you a good mix of easy questions and tough questions. Mechanical Engineering
students definitely take this Test: Strength of Materials Level - 3 exercise for a better result in the exam. You can find other Test: Strength of Materials Level - 3 extra questions,
long questions & short questions for Mechanical Engineering on EduRev as well by searching above.

QUESTION: 1

The stretch in a steel of circular section having a length L subjected to a tensile load P and tepering uniformly from a diameter d_{1} at one end to a diameter d_{2} at the other end, is given by

Solution:

QUESTION: 2

The total extension of the bar loaded as shown in the figure is A = area of cross-section E = modulus of elasticity

Solution:

QUESTION: 3

The deformation of a bar under its own weight as compared to that when subjected to a direct axial load equal to its own weight will be

Solution:

QUESTION: 4

A slender bar of 100 mm2 cross-section is subjected to loading as shown in the figure below. If the modulus of elasticity is taken as 200 × 109. pa. then the elongation produced in the bar will be

Solution:

QUESTION: 5

A straight bar is fixed at edges A and B. its elastic modulus is E and cross-section is A. There is a load P = 120 N acting at C. The reactions at the ends are

Solution:

QUESTION: 6

In a tensile test, near the elastic limit zone

Solution:

QUESTION: 7

If Poisson's ratio of a material is 0.5, then the elastic modulus for the material is

Solution:

QUESTION: 8

The number of independent elastic constants required to express the stress strain relationship for a linearly elastic isotropic material is

Solution:

QUESTION: 9

The number of elastic constants for a completely anisotropic elastic material is

Solution:

QUESTION: 10

For a given material, the modulus of rigidity is 100 GPa and Poisson's ratio is 0.25. The value of modulus of elasticity in GPa is

Solution:

QUESTION: 11

The volumetric strain in case of a thin cylindrical shell of diameter 'd', thickness 't', subjected to internal pressure 'P' is

Solution:

QUESTION: 12

The modulus of elasticity for a material is 200 GN/m^{2} and Poisson's ratio is 0.25. What is the modulus of rigidity ?

Solution:

QUESTION: 13

E, G, K andm represent the elastic modulus, shear modulus, Bulk modulus and poisson's ratio respectively of a linearly elastic. isotropic and homogeneous material. To express the stressstrain relations completely for this material, at least

Solution:

QUESTION: 14

What is the relationship between the linear elastic properties; Young's modulus (E), rigidity modulus (G) and bulk modulus (K) ?

Solution:

QUESTION: 15

A copper rod 400 mm long is pulled in tension to a length of 401.2 mm by applying a tensile stress of 330 MPa. If the deformation is entirely elastic, the Young's Modulus of copper is

Solution:

QUESTION: 16

Match List – I (State of stress) with List -II (kind of loading) and select the correct answer using the codes given below the lists:

Solution:

QUESTION: 17

State of stress at a point in a strained body is shown in figure A. which one of the figure given below represents correctly the mohr's circle for the state of stress?

Solution:

QUESTION: 18

Plane stress at a point in a body is defined by principal stresses 3s and s. The ratio of the normal stress to the maximum shear stress on the plane of maximum shear stress is

Solution:

QUESTION: 19

Which one of the following Mohr's circles represents the state of pure shear?

Solution:

QUESTION: 20

In a two dimensional problem the state of pure shear at a point is characterized by

Solution:

QUESTION: 21

A cantilever is loaded by a concentrated load P at the free and as shown. The shear stress in the element LMNOPQRS is under consideration

Which of the following figures represents the shear stress direction in the cantilever ?

Solution:

QUESTION: 22

A circular shaft subjected to twisting moment results in maximum shear stress of 60 MPa. Then the maximum compressive stress in the material is

Solution:

QUESTION: 23

Consider a two dimensional state of stress given for an element as shown in the diagram given below: What are the coordinates of the centre of Mohr's circle

Solution:

QUESTION: 24

A steel bar of 5 mm is heated from 25°C to 45°C and it is free to expand. The bar will induce

Solution:

Stress is nothing but the resisting force since due to temperature rise body will expand and if this expansion due to temperature change is restricted then only resisting stress (thermal stress) will come into play since expansion is not restricted that's why no stress is occurring.

QUESTION: 25

At a point in two-dimensional stress system s_{x} = 100 N/mm^{2},s_{y} =t_{xy}= 400 N/mm2. what drawn with a scale of 1cm = 100 N/mm^{2}.

Solution:

### Strength materials

Video | 48:16 min

### Strength of materials

Video | 50:40 min

### Strength of materials

Video | 58:23 min

### Strength of materials

Video | 57:57 min

- Test: Strength of Materials Level - 3
Test | 25 questions | 50 min

- Test: Strength of Materials - 3
Test | 25 questions | 50 min

- Test: Strength of Materials Level - 4
Test | 25 questions | 50 min

- Test: Strength of Materials Level - 1
Test | 25 questions | 50 min

- Strength of Materials - 3
Test | 20 questions | 12 min