Pavement Deterioration and its Types
Pavement deterioration is the process by which distress (defects) develop in the pavement under the combined effects of traffic loading and environmental conditions.
Types of pavement deterioration:
The four major categories of common asphalt pavement surface distresses are:
1.Cracking
2.Surface deformation
3.Disintegration (potholes, etc.)
4.Surface defects (bleeding, etc.)
A. Cracking: The most common types of cracking are:
1.Fatigue cracking
2.Longitudinal cracking
3.Transverse cracking
4.Block cracking
5.Slippage cracking
6.Reflective cracking
7.Edge cracking

1.Fatigue cracking (Alligator cracking): 
Fatigue cracking is commonly called alligator cracking. This is a series of interconnected cracks creating small, irregular shaped pieces of pavement. It is caused by failure of the surface layer or base due to repeated traffic loading (fatigue). Eventually the cracks lead to disintegration of the surface, as shown in Figure. The final result is potholes. Alligator cracking is usually associated with base or drainage problems. Small areas may be fixed with a patch or area repair. Larger areas require reclamation or reconstruction. Drainage must be carefully examined in all cases.

2.Longitudinal cracking: 
Longitudinal cracks are long cracks that run parallel to the center line of the roadway. These may be caused by frost heaving or joint failures, or they may be load induced. Understanding the cause is critical to selecting the proper repair. Multiple parallel cracks may eventually form from the initial crack. This phenomenon, known as deterioration, is usually a sign that crack repairs are not the proper solution.

3. Transverse cracking : 
Transverse cracks form at approximately right angles to the centerline of the roadway. They are regularly spaced and have some of the same causes as longitudinal cracks. Transverse cracks will initially be widely spaced (over 20 feet apart). They usually begin as hairline or very narrow cracks and widen with age. If not properly sealed and maintained, secondary or multiple cracks develop, parallel to the initial crack. The reasons for transverse cracking, and the repairs, are similar to those for longitudinal cracking. In addition, thermal issues can lead to low-temperature cracking if the asphalt cement is too hard.

4. Block cracking: 
Block cracking is an interconnected series of cracks that divides the pavement into irregular pieces. This is sometimes the result of transverse and longitudinal cracks intersecting. They can also be due to lack of compaction during construction. Low severity block cracking may be repaired by a thin wearing course. As the cracking gets more severe, overlays and recycling may be needed. If base problems are found, reclamation or reconstruction may be needed.

5. Slippage cracking: 
Slippage cracks are half-moon shaped cracks with both ends pointed towards the oncoming vehicles. They are created by the horizontal forces from traffic. They are usually a result of poor bonding between the asphalt surface layer and the layer below .The lack of a tack coat is a prime factor in many cases. Repair requires removal of the slipped area and repaving. Be sure to use a tack coat in the new pavement.

6. Reflective cracking: 
Reflective cracking occurs when a pavement is overlaid with hot mix asphalt concrete and cracks reflect up through the new surface. It is called reflective cracking because it reflects the crack pattern of the pavement structure below. As expected from the name, reflective cracks are actually covered over cracks reappearing in the surface. They can be repaired in similar techniques to the other cracking noted above. Before placing any overlays or wearing courses, cracks should be properly repaired.

7. Edge cracking: 
Edge cracks typically start as crescent shapes at the edge of the pavement. They will expand from the edge until they begin to resemble alligator cracking. This type of cracking results from lack of support of the shoulder due to weak material or excess moisture. They may occur in a curbed section when subsurface water causes a weakness in the pavement. At low severity the cracks may be filled. As the severity increases, patches and replacement of distressed areas may be needed. In all cases, excess moisture should be eliminated, and the shoulders rebuilt with good materials. Figure shows high severity edge cracking.
B. Surface deformation:
Pavement deformation is the result of weakness in one or more layers of the pavement that has experienced movement after construction. The deformation may be accompanied by cracking.
Surface distortions can be a traffic hazard.
The basic types of surface deformation are:
1.Rutting
2.Corrugations
3.Shoving
4.Depressions
5.Swell

1. Rutting 
Rutting is the displacement of pavement material that creates channels in the wheel path. Very severe rutting will actually hold water in the rut. Rutting is usually a failure in one or more layers in the pavement. The width of the rut is a sign of which layer has failed. A very narrow rut is usually a surface failure, while a wide one is indicative of a subgrade failure. Inadequate compaction can lead to rutting. Figure shows an example of rutting due to subgrade Failure. Minor surface rutting can be filled with micro paving or paver-placed surface treatments. Deeper ruts may be shimmed with a truing and leveling course, with an overlay placed over the shim. If the surface asphalt is unstable, recycling of the surface may be the best option. If the problem is in the subgrade layer, reclamation or reconstruction may be needed.

2. Corrugation 
Corrugation is referred to as wash boarding because the pavement surface has become distorted like a wash board. The instability of the asphalt concrete surface course may be caused by too much asphalt cement, too much fine aggregate, or rounded or smooth textured coarse aggregate. Corrugations usually occur at places where vehicles accelerate or decelerate. Minor corrugations can be repaired with an overlay or surface milling. Severe corrugations require a deeper milling before resurfacing.

3. Shoving 
Shoving is also a form of plastic movement in the asphalt concrete surface layer that creates a localized bulging of the pavement. Locations and causes of shoving are similar to those for corrugations. Repair minor shoving by removing and replacing. For large areas, milling the surface may be required, followed by an overlay.

4. Depressions 
Depressions are small, localized bowl-shaped areas that may include cracking. Depressions cause roughness, are a hazard to motorists, and allow water to collect. Depressions are typically caused by localized consolidation or movement of the supporting layers beneath the surface course due to instability. Repair by excavating and rebuilding the localized depressions. Reconstruction is required for extensive depressions.

5. Swell 
A swell is a localized upward bulge on the pavement surface. Swells are caused by an expansion of the supporting layers beneath the surface course or the subgrade. The expansion is typically caused by frost heaving or by moisture. Subgrades with highly plastic clays can swell in a manner similar to frost heaves (but usually in warmer months). Repair swells by excavating the inferior subgrade material and rebuilding the removed area. Reconstruction may be required for extensive swelling.

C. Disintegration 
The progressive breaking up of the pavement into small, loose pieces is called disintegration. If the is integration is not repaired in its early stages, complete reconstruction of the pavement may be needed.
The two most common types of disintegration are:
1.Potholes
2.Patches

1.Potholes 
Potholes are bowl-shaped holes similar to depressions. They are a progressive failure. First, small fragments of the top layer are dislodged. Over time, the distress will progress downward into the lower layers of the pavement. Potholes are often located in areas of poor drainage, as seen in Figure. Potholes are formed when the pavement disintegrates under traffic loading, due to inadequate strength in one or more layers of the pavement, usually accompanied by the presence of water. Most potholes would not occur if the root cause was repaired before development of the pothole. Repair by excavating and rebuilding. Area repairs or reconstruction may be required for extensive potholes.
2. Patches: 
A patch is defined as a portion of the pavement that has been removed and replaced. Patches are usually used to repair defects in a pavement or to cover a utility trench. Patch failure can lead to a more widespread failure of the surrounding pavement. Some people do not consider patches as a pavement defect. While this should be true for high quality patches as is done in a semi permanent patch, the throw and roll patch is just a cover. The underlying cause is still under the pothole. To repair a patch, a semi-permanent patch should be placed. Extensive potholes may lead to area repairs or reclamation. Reconstruction is only needed if base problems are the root source of the potholes.

D. Surface defects: 
Surface defects are related to problems in the surface layer. The most common types of surface distress are:
1.Ravelling
2.Bleeding
3.Polishing
4.Delamination

1. Ravelling: 
Ravelling is the loss of material from the pavement surface. It is a result of insufficient adhesion between the asphalt cement and the aggregate. Initially, fine aggregate breaks loose and leaves small, rough patches in the surface of the pavement. As the disintegration continues, larger aggregate breaks loose, leaving rougher surfaces. Ravelling can be accelerated by traffic and freezing weather. Some ravelling in chip seals is due to improper construction technique. This can also lead to bleeding. Repair the problem with a wearing course or an overlay.
2. Bleeding: 
Bleeding is defined as the presence of excess asphalt on the road surface which creates patches of asphalt cement. Excessive asphalt cement reduces the skid-resistance of a pavement, and it can become very slippery when wet, creating a safety hazard. This is caused by an excessively high asphalt cement content in the mix, using an asphalt cement with too low a viscosity (too flowable), too heavy a prime or tack coat, or an improperly applied seal coat. Bleeding occurs more often in hot weather when the asphalt cement is less viscous (more flowable) and the traffic forces the asphalt to the surface. Figure 13 shows an example of bleeding during hot weather.
3. Polishing: 
Polishing is the wearing of aggregate on the pavement surface due to traffic. It can result in a dangerous low friction surface. A thin wearing course will repair the surface.

Offer running on EduRev: Apply code STAYHOME200 to get INR 200 off on our premium plan EduRev Infinity!

Dynamic Test

Content Category

Related Searches

Viva Questions

,

past year papers

,

Extra Questions

,

video lectures

,

Exam

,

ppt

,

mock tests for examination

,

Pavement Deterioration and its Types Civil Engineering (CE) Notes | EduRev

,

Semester Notes

,

Free

,

pdf

,

shortcuts and tricks

,

Summary

,

Previous Year Questions with Solutions

,

Pavement Deterioration and its Types Civil Engineering (CE) Notes | EduRev

,

MCQs

,

study material

,

practice quizzes

,

Sample Paper

,

Pavement Deterioration and its Types Civil Engineering (CE) Notes | EduRev

,

Important questions

,

Objective type Questions

;