Question for GATE Past Year Questions: Fatigue Strength & S-N Diagram
Try yourself:Endurance limit of a beam subjected to pure bending decreases with
[2019 , Set 2]
Question for GATE Past Year Questions: Fatigue Strength & S-N Diagram
Try yourself:A cylindrical shaft is subjected to an alternating stress of 100 MPa. Fatigue strength to sustain 1000 cycles is 490 MPa. If the corrected endurance strength is 70 MPa, estimated shaft life will be
[2006]
Explanation
By concept of straight line,
At y = 2
⇒ x = 5.4501
log10N = 5.4501, N = 281914
Report a problem
Question for GATE Past Year Questions: Fatigue Strength & S-N Diagram
Try yourself:The S-N curve for steel becomes asymptotic nearly at
[2004]
Question for GATE Past Year Questions: Fatigue Strength & S-N Diagram
Try yourself:In terms of theoretical stress concentration factor kt and fatigue stress concentration factor kt, the notch sensitivity q is expressed as
[2004]
Question for GATE Past Year Questions: Fatigue Strength & S-N Diagram
Try yourself:Which one of the following is the most conservation fatigue failure criterion?
[2015, Set-1]
Question for GATE Past Year Questions: Fatigue Strength & S-N Diagram
Try yourself:A static load is mounted at the centre of a shaft rotating at uniform angular velocity. This shaft will be designed for
[2002]
Explanation
Shaft will be designed for fatigue loading.
Report a problem
Question for GATE Past Year Questions: Fatigue Strength & S-N Diagram
Try yourself:The yield strength of a steel shaft is twice its endurance limit. Which of the following torque fluctuations represent the most critical situation according to Soderberg criterion?
[1993]
Explanation
τa is highest in (a)
Report a problem
Question for GATE Past Year Questions: Fatigue Strength & S-N Diagram
Try yourself:The process of shot peening increases the fatigue life of steel springs mainly because it results in
[1990]
Explanation
Shot preening increases fatigue life of springs
Report a problem
Question for GATE Past Year Questions: Fatigue Strength & S-N Diagram
Try yourself:Stress concentration in a machine component of a ductile material is not so harmful as it is in a brittle material because
[1989]
Explanation
Local yielding reduces stress concentration effect.
Report a problem
Question for GATE Past Year Questions: Fatigue Strength & S-N Diagram
Try yourself:A ductile material having an endurance limit of 196 N/mm2 and the yield point at 294 N/mm2 is stressed under variable load. The maximum and minimum stresses are 147 N/mm2 and 49 N/mm2. The fatigue stress concentration factor is 1.32. The available factor of safety for this loading is
[1987]
Explanation
Consider Soderberg equation
FOS = 1.5
Report a problem