Test: Concrete Technology- 2 - Civil Engineering (CE) MCQ

The process of manufacturing of white Portland cement is same as of OPC but the amount of iron oxide which is responsible for greyish colour is limited to less than 1%.

Air entrainment is the intentional creation of tiny air bubbles in concrete. The air bubbles are created during mixing of the plastic (easy flowing) concrete, and most of them survive to be part of the hardened concrete. The primary purpose of air entrainment is to increase the durability of the hardened concrete, especially in climates subject to freeze-thaw; the secondary purpose is to increase workability of the concrete while in a plastic state. Air entrained concrete increases the workability of concrete without much increase in water-cement ratio.

Vicat’s Apparatus is used to find out the consistency, initial setting time and final setting time of the cement. In the normal consistency test we have to find out the amount of water to be added to the cement to form a cement paste of normal consistency. Vicat's apparatus consists of an arrangement to hold the plunger of 10 mm diameter and two other needles which are made to freely fall into a mould filled with the cement paste and the amount of penetration of the needles of plunder can be noted using the vertical graduations from 0 mm to 50 mm.

For determination of initial setting time: The needle of diameter 1 mm is used.

Initial setting time shall not be less than 30 minutes and final setting time should not be more than 10 hours.

The loading plates and the top/bottom surface of the concrete specimen offers some frictional resistance called as platen restraint which introduces shear stress at the top and bottom surfaces of the specimen and this effect diminishes as the distance between the platen surface increases. For this reason, standard concrete cube (height/diameter ratio = 1) specimen gives higher compressive strength then the cylindrical specimen (height/diameter ratio = 2).

Cube strength of concrete is nearly 1.25 times the cylindrical strength.

So, the ratio of strength of concrete cube to that of concrete cylinder is 1.25.

Ultrasonic Pulse velocity method deals with the noting of time of travel of electronically generated mechanical pulse which is further used to analyse the velocity of pulse through the structure that represents its quality.

This test is used to establish uniformity of concrete, estimation of pulse modulus of elasticity, estimation of strength of concrete, determination of setting characteristics of concrete, estimation of crack depth, measurement of thickness of concrete pavement. This test calculates dynamic modulus of elasticity of concrete.

This test does not estimate tensile strength of concrete, so option a, b, d are wrong. So, correct answer is option c.

If rounded aggregates are used in the concrete, it results in highly workable mixture as it offers minimum surface area to be lubricated by water cement paste. If angular aggregates are used, it will result in the high strength concrete while flaky aggregate in concrete neither possess strength nor any workability.

Generally, almost all pumped concrete is conveyed through 125 mm pipeline. General rule is that the pipe diameter should be between 3 to 4 times the largest size of aggregate. Concrete has been pumped to a height over 400 m and a horizontal distance of over 2000 m. But the diameter of the pipeline used for transportation of concrete by pumps should not exceed 30 cm.

The finishing of concrete surface is finally achieved by the following operations:

1. Screeding: it is the levelling operation that removes humps and hollows and give a true and uniform concrete surface.

2. Floating: It is the process of removing the irregularities from the surface of concrete left after screeding.

3. Trowelling: It is the final operation of finishing the concrete surface. It is performed where smooth and dense surface is required.

4. Curing: It is the process of hardening the concrete mixes by keeping its surface moist for a certain period, in order to enable the concrete to gain more strength.

Durability of concrete may be defined as the ability of concrete to resist weathering action, chemical attack, and abrasion while maintaining its desired engineering properties. For a durable concrete, use of lowest w/c ratio is the fundamental requirement to produce dense and impermeable concrete. Lowering the water-cement ratio will lead to increase in the cement content thus increasing the durability. Mix must be designed to ensure cohesion and prevent segregation and bleeding. If cement is reduced, then at fixed w/c ratio the workability will be reduced leading to inadequate compaction. However, if water is added to improve workability, water / cement ratio increases and resulting in highly permeable material.

For concrete work low workable concrete is preferred.

∴ Slump value for concrete roads = (20 – 30) mm

Normal RCC work = (80 – 150) mm

Mass concrete = (20 – 50) mm

Columns and slabs = (40 – 50) mm

The modulus of rupture test employs a 150 × 150 × 700 mm plain concrete beam. The beam is simply supported and subjected to third-points loading until failure. Assuming a linear stress distribution across the cross-section, the theoretical maximum tensile stress reached in the extreme fibre is termed the modulus of rupture (f_cr). It is obtained by applying the flexure formula.

Modulus of rupture is given by

As slump increases, Vee bee time decreases, as it becomes easier for concrete to flow.

It is clear from the below figure that as the slump increases, the compaction factor also increases.

Steel mould used to measure slump value is shown below:

The ratio of bottom mould to top mould is 

The nominal mixes of fixed cement-aggregate ratio (by volume) vary widely in strength and may result in under- or over-rich mixes. For this reason, the minimum compressive strength has been included in many specifications. These mixes are termed standard mixes.

IS 456-2000 has designated the concrete mixes into a number of grades as M10, M15, M20, M25, M30, M35 and M40. In this designation the letter M refers to the mix and the number to the specified 28 day cube strength of mix in N/mm². The mixes of grades are as follows:

As per IS 456 and IS 1343, the design of concrete mix should be based on the following factors:

• Characteristic compressive strength.
• Type of cement
• Maximum Nominal Size of Aggregate
• Grading of Combined Aggregate
• Water-Cement Ratio
• Workability
• Durability
• Degree of quality control

As per IS 456:2000, to prevent segregation, the maximum height for placing concrete is 150 cm.

Please refer IS 456:2000 section 13.2 " As a general guidance, the maximum permissible free fall of concrete may be taken as 1.5 m." 

The strength of concrete depends both on temperature during curing and period of curing, and strength can be visualized as a function of period and temperature. The product (period x temperature) is called maturity of concrete. Here the temperature is taken from -10 degree Celsius which is the reasonable lowest value of temperature at which an appreciable increase in strength can take place. The maturity is measured in °C hours  or °C days.

In bacterial concrete when cracks appear in a concrete structure and water starts to seep in through, the spores of the bacteria start microbial activities on contact with the water and oxygen. In the process of precipitating calcite crystals through nitrogen cycle the soluble nutrients are is converted to insoluble CaCO3 and remediate the cracks.