Match the correct combination for following metal working processes. 

A metal disc of 20 mm diameter is to be punched from a sheet of 2 mm thickness. The punch and the die clearance is 3%. The required punch diameter is 

10 mm diameter holes are to be punched in a steel sheet of 3 mm thickness. Shear strength of the material is 400 N / mm² and penetration is 40%. Shear provided on the punch is 2 mm.The blanking force during the operation will be 

Match List-I (metal forming process) with List-II (Associated feature) and select the correct answer using the codes given below the Lists:

In a blanking operation to produce steel washer, the maximum punch load used in 2 x 10⁵ N.The plate thickness is 4 mm and percentage penetration is 25. The work done during this shearing operation is 

A 50 mm diameter disc is to be punched out from a carbon steel sheet 1.0 mm thick. The diameter of the punch should be 

Worm working or semi-hot working process, which is the plastic deformation of metal or alloy under conditions of temperature and strain rate, is performed to eliminate drawbacks of 

Match List I (Operation) with List II (Explanation) and select the correct answer using the
codes given below the Lists:

In deciding the clearance between punch and die in press work in shearing, the following rule is helpful: 

Consider the following steps in forging a connecting rod from the bar stock:
1. Blocking
2. Trimming
3. Finishing
4. Edging

Select the correct sequence of these operations using the codes given below: 

Codes:

A hole is to be punched in a 15 mm thick plate having ultimate shear strength of 3N-mm^-2. If the allowable crushing stress in the punch is 6 N-mm^-2, the diameter of the smallest hole which can be punched is equal to 

The order of radial clearance between the punch and die for shearing a steel plate of thickness ‘t’ (1 mm ≤2 mm) is 

Which one of the following factor promotes the tendency for wrinking in the process of drawing? 

The mode of deformation of the metal during spinning is 

Which one of the following is a continuous bending process in which opposing rolls are used to produce long sections of formed shapes from coil or strip stock? 

A 1.5 mm thick sheet is subject to unequal biaxial stretching and the true strains in the directions of stretching are 0.05 and 0.09. The fh'1al thickness of the sheet in mm is 

Consider the following statements:
Earring in a drawn cup can be due to non-uniform
1. speed of the press 2. clearance between tools
3. material properties 4. blank holding 

Q. Which of these statements are correct?